Hauthane HD-2602 was designed primarily for topcoat applications where slip and abrasion resistance properties are required. Hauthane HD-2602 contains a non-fugitive silicone component that provides low surface tension characteristics on flexible and rigid substrates including plastics, metals and textiles.
- Product Applications
Hauthane HD-2602 may be used as a sole vehicle or blended with acrylic emulsions for spray or rotogravure applications. Rheology modifications can be made with associative thickeners for alternative application methods.
- Drying
Hauthane HD-2602 can be air dried, if desired, depending on film thickness. Typical oven drying temperatures and dwell times for aqueous coatings are sufficient to produce optimal film properties.
Properties
- Physical Form
- Physical Properties
Value Units Test Method / Conditions Solid Content 34 - 36 % - Viscosity 50 - 500 cPs - pH 7.0 - 9.5 - - Density 8.7 Ibs/gal - Softening Point 305 °F - Volatile Organic Compounds (as Supplied) 105 gm/l - Volatile Organic Compounds (less Water) 243 gm/l - Sward Hardness 35 - - - Tensile Properties
Value Units Test Method / Conditions 100% Modulus (Tested at 20 Inches/minute) 3180 psi - 200% Modulus (Tested at 20 Inches/minute) 4610 psi - 300% Modulus (Tested at 20 Inches/minute) NA - - Elongation (Tested at 20 Inches/minute) 300 % - Tensile Strength (Tested at 20 Inches/minute) min. 6375 psi - - Product Characteristics
- May be formulated into low surface tension coatings
- Excellent abrasion resistance
- Non-fugitive silicone component
- Crosslinkable for improved adhesion and performance
- Contains n-methyl pyrrolidone co-solvent